Stainless steel 410 is produced in accordance with the American ASTM standard of stainless steel, equivalent to China's 1Cr13 stainless steel, S41000 (AISI, ASTM).
0.15% carbon, 13% chromium,410 stainless steel: good corrosion resistance, machinability, general purpose blade, valve type.
Heat treatment of stainless steel: solution treatment (℃) 800-900 slow cooling or 750 fast cooling
1) High strength;
2) Excellent machinability
3) Hardened after heat treatment;
4) Magnetic;
5) not suitable for harsh corrosive environment.
Scope of application
General blade, mechanical parts, class 1 tableware (spoon, fork, knife, etc.).
This is the most cost effective grade of steel. So the 410 Stainless Steel perforated plate Price is lower compared to other grades of stainless steels and all metallic products in general. There are different versions of the material with low carbon and high carbon content. The low carbon version, 410 perforated plate are very good for welding applications as they have less carbide precipitation and less localized corrosion.
Equivalent Grades
| Grade |
UNS |
WNR. |
Japanese JIS |
| No. |
| 410 |
S41000 |
1.4550 |
SUS410 |
Standard Specification
| Thickness |
0.1mm-12mm |
| Width |
1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc |
| Length |
Customized |
| Surface |
2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, checkered, embossed, hair line, sand blast, Brush, etching, etc |
| Finish |
Hot rolled coil (HR), Cold rolled coil (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated) |
| Form |
Round hole, square hole, diamond hole, hexagonal hole, waist round hole, rectangular hole, triangular hole, pattern hole, non-standard hole, large and small holes, gradient hole, cross hole, plum blossom hole |
Composition content
| Grade |
C |
Mn |
Si |
P |
S |
Cr |
Mo |
Ni |
N |
| 410 |
Min.
Max. |
≤0.15 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.03 |
11.50~13.50 |
/ |
|
|
410 stainless steel perforated plate mechanical properties
| Grade |
mechanical properties |
| Ys (Mpa) |
Ts (Mpa) |
El (%) |
Hv |
| 410 |
≥ 205 |
≥ 440 |
≥ 20 |
≤ 210 |
410 stainless steel perforated plate physical parameters
| density (g/cm) |
magnetic |
specific heat 25℃(J/kg.℃) |
Thermal conductivity 100℃(W/m.℃) |
thermal expansion rate20~100℃(10/℃) |
| 7.7 |
yes |
460 |
24.9 |
9.9 |
Characteristic machining technology
2B -- Silver white with better gloss and flatness than a 2D surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + quenching and tempering rolling.
Ba - Excellent surface gloss, high reflectivity, like a mirror surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + surface polishing + quenching and tempering rolling.
No.3 -- Good gloss, coarse grain surface.
Processing technology: polishing and tempering rolling for 2D or 2B with 100~120 abrasive materials (JIS R6002).
No.4 -- Good gloss, fine lines on the surface.
Processing process: polishing and tempering rolling for 2D or 2B with 150~180 abrasive materials (JIS R6002).
HL -- Silver grey with hair streaks.
Processing technology: 2D products or 2B products with appropriate granularity of abrasive materials for polishing the surface is a continuous abrasive grain.
MIRRO -- Specular.