405 stainless steel is a composite steel that does not harden significantly when cooled from high temperatures.
405 Stainless steel sheet Price in China ,Manufacturer of 405 Stainless Steel sheet
405 is equivalent to China's 0Cr13Al stainless steel, cooling from high temperature does not produce significant hardening.
405 stainless steel used as steam turbine material, quenching parts, composite steel.
This is the most cost effective grade of steel. So the 405 Stainless Steel Sheet Price is lower compared to other grades of stainless steels and all metallic products in general. There are different versions of the material with low carbon and high carbon content. The low carbon version, 405 sheets are very good for welding applications as they have less carbide precipitation and less localized corrosion.
Equivalent Material of 405 Stainless Steel Sheet
| Grade |
Euronorm |
China GB |
Japanese JIS |
| No. |
| 405 |
1.4002 |
0Cr13Al |
SUS405 |
Standard Specification Of 405 Plate
| Thickness |
4mm-100mm |
| Width |
1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc |
| Length |
2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc |
| Surface |
2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, checkered, embossed, hair line, sand blast, Brush, etching, etc |
| Finish |
Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated) |
| Form |
Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats,
Blank (Circle), Ring (Flange) etc. |
405 stainless steel composition content.
| Grade |
C |
Mn |
Si |
P |
S |
Cr |
Mo |
Ni |
Al |
| 405 |
Min.
Max. |
≤0.08 |
≤1.00 |
≤1.00 |
≤0.04 |
≤0.03 |
11.5~14.5 |
/ |
≤0.60 |
0.10~0.30 |
| |
|
|
|
|
|
|
|
|
|
|
Annealing treatment/(℃) : 780-830 fast cooling or slow
Tensile test: σ0.2 / MPa ≧ 177;
Sigma b/Mpa ≧ 410;
Δ5 (%) ≥ 20;
Ψ (%) ≧ 60;
Impact test: AK /J 78
Hardness test: HBW≤183