304 wire can withstand high temperatures up to 870 degrees Celsius. The wires are used for this reason in evaporators, heat exchangers and in other high temperature applications. The Stainless Steel 304 wire is also used in drums, barrels, dairy equipment, food processing and in hospital equipment.
This is the most cost effective grade of steel. So the 304 Stainless Steel wire Price is lower compared to other grades of stainless steels and all metallic products in general. There are different versions of the material with low carbon and high carbon content. The wires and UNS S30400 Stainless Steel Strip Specification varies and the applications differ for the different versions of the material. The low carbon version, 304L wires are very good for welding applications as they have less carbide precipitation and less localized corrosion. The ASME SA240 Stainless Steel 304 wire Thickness ranges up to 200mm and the width and the length ranges widely depending on the application requirements as well. Please contact us for more information and prices.
This is the most cost effective grade of steel. So the 304 Stainless Steel wire Price is lower compared to other grades of stainless steels and all metallic products in general. There are different versions of the material with low carbon and high carbon content. The low carbon version, 304 wires are very good for welding applications as they have less carbide precipitation and less localized corrosion.
Equivalent Grades
| Grade |
Euronorm |
China GB |
Japanese JIS |
| No. |
| 304 |
1.4301 |
0Cr18Ni9 |
SUS304 |
Standard Specification
| Diameter |
0.1mm-8.0mm |
| Length |
Customized as you wished |
| Cross-sectional shape |
Since the custom |
| Surface |
Polished, 2B, Mirror, Brush,etc |
| Finish |
Drawing, welding, drilling, forging, surface treatment, slitting |
| Application |
For automobiles, solar energy, metal products, household appliances, precision electronics, sanitary ware |
Composition content
| Grade |
C |
Mn |
Si |
P |
S |
Cr |
Mo |
Ni |
N |
| 304 |
Min.
Max. |
≤0.08 |
≤2.00 |
≤0.75 |
≤0.045 |
≤0.03 |
18.0～20.0 |
/ |
8.0-10.50 |
≤0.25 |
Tensile strength :515MPa
Yield strength :205MPa
Elongation 40%
Elastic modulus :29,000,000 psi is equivalent to: 203000MPa
Hardness requirement (Brinell hardness)
92 n/was (MPa).
Density :.280 LBS /cubic inch(density 7.93g/cm3)
Characteristic machining technology
1D -- The surface has discontinuous granular shape, also known as fog surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling.
2D - A slightly silvery white colour.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling.
2B -- Silver white with better gloss and flatness than a 2D surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + quenching and tempering rolling.
Ba - Excellent surface gloss, high reflectivity, like a mirror surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + surface polishing + quenching and tempering rolling.
No.3 -- Good gloss, coarse grain surface.
Processing technology: polishing and tempering rolling for 2D or 2B with 100~120 abrasive materials (JIS R6002).
No.4 -- Good gloss, fine lines on the surface.
Processing process: polishing and tempering rolling for 2D or 2B with 150~180 abrasive materials (JIS R6002).
HL -- Silver grey with hair streaks.
Processing technology: 2D products or 2B products with appropriate granularity of abrasive materials for polishing the surface is a continuous abrasive grain.
MIRRO -- Specular.
Processing technology: 2D products or 2B products with appropriate granularity of the grinding material grinding and polishing to the mirror effect.